Potassium Titanyl Arsenate (KTiOAsO4), or KTA crystal, is an excellent nonlinear optical crystal for Optical Parametric Oscillation (OPO) application. It has better non-linear optical and electro-opti..
Potassium Titanyl Arsenate (KTiOAsO4), or KTA crystal, is an excellent nonlinear optical crystal for Optical Parametric Oscillation (OPO) application. It has better non-linear optical and electro-optical coefficients, significantly reduced absorption in the 2.0-5.0 µm region, broad angular and temperature bandwidth, low dielectric constants. And its low ionic conductivities result in higher damage threshold compared with KTP .
Crystal Structure
|
Orthorhombic, point group mm2,
|
Lattice Parameter
|
a=13.125Å, b=6.5716Å, c=10.786Å
|
Melting Point
|
1130 ˚C
|
Mohs Hardness
|
near 5
|
Density
|
3.454g/cm3
|
Thermal Conductivity
|
K1:1.8W/m/K; K2: 1.9W/m/K; K3: 2.1W/m/K
|
Transparency Range
|
350-5300nm
|
||||
Absorption Coefficients
|
@ 1064 nm <0.05 %/cm
@ 1533 nm <0.05 %/cm @ 3475 nm <5%/cm
|
||||
NLOSusceptibilities (pm/V)
|
d31 = 2.76, d32 = 4.74, d33 = 18.5 , d15 = 2.3, d24 = 3.2
|
||||
Sellmeier Equation
N i 2=A i +Bi λ2/(λ2-Ci 2)-Di λ2
(l in mm)
|
index
|
A
|
B
|
C
|
D
|
nx
|
1.90713
|
1.23522
|
0.19692
|
0.01025
|
|
ny
|
2.15912
|
1.00099
|
0.21844
|
0.01096
|
|
nz
|
2.14768
|
.29559
|
.22719
|
0.01436
|
|
Electro-optical Constants (pm/V) (low frequency)
|
r33=37.5; r23=15.4; r13=11.5
|
||||
SHG Phase Matchable Range
|
1083-3789nm
|