RAYSERS KTP crystals feature high purity, low absorption at fundamental and second harmonic generation wavelengths. We supply superior grade and customer-designed KTP crystals for various applications..
RAYSER’S KTP crystals feature high purity, low absorption at fundamental and second harmonic generation wavelengths. We supply superior grade and customer-designed KTP crystals for various applications.
|
Crystal Structure
|
Orthorhombic, space group Pna21,point group mm2
|
|
Lattice Parameter
|
a=6.404Å, b=10.616Å, c=12.814A, Z=8
|
|
Melting Point
|
About 1172°C
|
|
Mohs Hardness
|
5
|
|
Density
|
3.01 g/cm3
|
|
Thermal Conductivity Coefficient
|
13W/m/K
|
|
Thermal Expansion Coefficient
|
ax=11x10-6/℃, ay=9x10-6/℃, az=0.6x10-6/℃
|
|
Transparency Range
|
350~4500nm
|
|
SHG Phase Matchable Range
|
497 ~ 1800nm (Type II)
|
|
Thermal-optic Coefficients (/°C)
|
dnx/dT=1.1X10-5
dny/dT=1.3X10-5 dnz/dT=1.6X10-5 |
|
Absorption Coefficients
|
<0.1%/cm at 1064nm <1%/cm at 532nm
|
|
For Type II SHG of a Nd:YAG laser at 1064nm
|
Temperature Acceptance: 24°C·cm
Spectral Acceptance: 0.56nm·cm Angular Acceptance: 14.2mrad·cm (φ);55.3mrad·cm (θ) Walk-off Angle: 0.55° |
|
NLO Coefficients
|
deff(II)≈(d24 - d15)sin2Φsin2θ - (d15sin2Φ + d24cos2Φ)sinθ
|
|
Non-vanished NLO Susceptibilities
|
d31=6.5 pm/V d24=7.6 pm/V
d32= 5 pm/V d15=6.1 pm/V d33=13.7 pm/V |
|
Electro-optic Coefficients:
r13
r23
r33
r51
r42
|
Low frequecy(pm/V) High frequency(pm/V)
9.5 8.8
15.7 13.8
36.3 35.0
7.3 6.9
9.3 8.8
|
|
Dielectric Constant
|
εeff=13
|
|
Sellmeier Equations
(λ in μm)
|
nx2=3.0065+0.03901/(λ2-0.04251)-0.01327λ2
ny2=3.0333+0.04154/(λ2-0.04547)-0.01408λ2 nz2=3.3134+0.05694/(λ2-0.05658)-0.01682λ2 |