Language
Co2+:MgAl2O4 is a relatively new material for passive Q-switching in lasers emitting from 1.2 to 1.6 m, in particular, for eye-safe 1.54 m Er:glass laser, but also works at 1.44 m and 1.34 m wavelengt..
Co2+:MgAl2O4 is a relatively new material for passive Q-switching in lasers emitting from 1.2 to 1.6 μm, in particular, for eye-safe 1.54 μm Er:glass laser, but also works at 1.44 μm and 1.34 μm wavelengths. Spinel is a hard, stable crystal that polishes well. Cobalt substitutes readily for magnesium in the Spinel host without the need for additional charge compensation ions. High absorption cross section (3.5×10-19 cm2) permits Q-switching of Er:glass laser without intracavity focusing both with flash-lamp and diode-laser pumping. Negligible excited-state absorption results in high contrast of Q-switch, i.e. the ratio of initial (small signal) to saturated absorption is higher than 10.
|
Attributes
|
value
|
|
Chemical Formula
|
Co2+:MgAl2O4
|
|
Crystal Structure
|
cube
|
|
Lattice Constant
|
8.07Å
|
|
Density
|
3.62 g/cm3
|
|
Melting Point
|
2105°C
|
|
Reflective Index
|
n=1.6948 @1.54μm
|
|
Stimulated Emission Cross Section
|
0.033W
|
|
Specific heat capacity/(J·g-1·K-1)
|
1.046
|
|
Thermal expansion coefficient/（10-6/℃@25℃）
|
5.9
|
|
Mohs hardness
|
8.2
|
|
Extinction Ratio
|
25dB
|
|
Lattice orientation
|
[100] or [111] < ±0.5°
|
|
Optical density
|
0.1-0.9
|
|
Damage threshold
|
>500 MW/cm2
|
|
Co2+ doping concentration
|
0.01-0.3 atm%
|